Environment-Friendly Polymer Additives
ADK CYCLOAID PNB-205
Properties | Liquid | ||
---|---|---|---|
Packaging | C/N 16kg D/M 180kg |
||
Characteristics and applications | ・Excellent oil resistance, heat aging stability, and less-migration to other plastics. ・For PVC Film, Sheet, and daily-use industrial products, etc |
||
Composition | polyester |
Data of ADK CYCLOAID PNB-205
|
PNB-205 |
DOP |
DOTP |
Epoxy type |
Polyester type |
|
---|---|---|---|---|---|---|
Viscosity (mPa・s/25℃) |
mPa・s |
500 |
60 |
60 |
380 |
500 |
Color tone stability |
||||||
180℃×5min, 2mm |
Y.I |
14.0 |
11.7 |
13.1 |
15.7 |
12.3 |
Transparency |
||||||
180℃×5min, 2mm |
Haze |
2.6 |
1.9 |
2.1 |
2.3 |
2.9 |
Electrical insulating |
||||||
Volume intrinsic resistance |
Ω・cm |
1.0 |
10.0 |
16.8 |
4.9 |
1.1 |
Cold resistance |
||||||
Clash-Berg (Tf) |
℃ |
-20.1 |
-25.8 |
-26.7 |
-14.3 |
-14.0 |
Migration test |
||||||
ABS (70℃) |
* |
± |
-- |
-- |
± |
± |
Tensil testing |
||||||
Tensil strength |
MPa |
22.6 |
20.1 |
22.2 |
22.2 |
22.5 |
100% modulus |
MPa |
12.0 |
10.6 |
11.2 |
11.4 |
11.7 |
Elongation |
% |
360 |
350 |
350 |
340 |
320 |
Heat aging stability 100℃×120h |
||||||
Volatile loss |
% |
1.2 |
3.0 |
1.1 |
0.3 |
1.2 |
Elongation retention |
% |
98 |
92 |
95 |
99 |
97 |
Oil resistance 100℃×96h ASTM No.2 oil |
||||||
Extracted volume |
% |
11.4 |
16.2 |
15.0 |
11.0 |
11.4 |
Compatibility 40℃×80%RH×4 weeks |
||||||
Bleeding |
* |
+ |
++ |
+ |
- |
+ |
* ++: Excellent, +: Good, -: Average, --: Poor
Composition:PVC(p=1,050)100 / Stabilizer (Ba-Zn) 2.5 / Plasticizer 50